Fabricación de tableros aglomerados de partículas de la especie hevea brasiliensis (caucho) con resina sintética del tipo urea formaldehido
Fecha
2023-06-15Autor
Palabras Clave
Tableros aglomerados de partículas, Resinosidad, Urea formaldehido, Hevea brasiliensis, CauchoParticleboards, Resinosity, Formaldehyde urea, Hevea brasiliensis, Rubber
Metadatos
Mostrar el registro completo del ítemResumen
Hevea brasiliensis de 25 años de edad proveniente de la plantación del Campo Comparativo de Trapichote del Orinoco, Estado Amazonas, fue utilizado en la elaboración experimental de tableros aglomerados de partículas a dos niveles de densidad teórica (nominal) de 0,600 g/cm3 y0,800 g/cm3, a un nivel de contenido de resina de urea formaldehido del 8%, 7% de catalizador de sulfato de amonio al 30% de concentración, a un contenido de humedad del colchón al momento del prensado de aproximadamente 12% y a dos tiempos de prensado de 5 a 20 minutos.
Las propiedades físicas y mecánicas de los tableros fueron determinadas siguiendo las estipulaciones de las Normas Alemanas DIN y Venezolanas Covenin 847.91. Las propiedades físicas fueron la absorción de agua y la variación de espesor o estabilidad dimensional a las 2 y 24 horas por inmersión total en agua, las propiedades mecánicas fueron la resistencia a la flexión (módulo de ruptura) y tracción perpendicular a la superficie del tablero.
Las propiedades físicas de absorción de agua a 2 y 24 horas de inmersión para tableros de densidad 0,600 g/cm3 no cumplen con los requerimientos máximo estipulados por la Norma Covenin 847.91. La absorción de agua a 2 horas de inmersión para tableros de 0,600 g/cm3 de densidad no cumplen con el valor máximo de 25% estipulado por la norma, los tableros de densidad 0,800 g/cm3 a 24 horas de inmersión si cumplen con los estipulado por la Norma. La variación de espesor 0,800 g/cm3 de densidad no cumple con los valores máximos estipulados por la Norma. La variación de espesor para 24 para tableros con 0,600 g/cm3 y 0,800 g/cm3 de densidad si cumplen con los máximos estipulados por la Norma Covenin 847.91. Los valores obtenidos de las propiedades mecánicas de Flexión Estática y Tracción Perpendicular para tableros de densidad 0,600 g/cm3 y 0,800 g/cm3 cumplen cabalmente con las exigencias de la Norma Covenir 847.91 y DIN.
Información Adicional
Otros Títulos | Production of particle board of the specie hevea braziliensis (rubber) with synthetic resin of the type formaldehyde urea |
Correo Electrónico | dargaray@ula.ve jorduran@ula.ve pmoreno@ula.ve ifla@ula.ve ifla@ula.ve |
ISSN | 0798-2437 |
Resumen en otro Idioma | Twenty five years-old, Hevea brasiliensis trees from the plantation of the comparative field of Trapichote of the Orinoco, Amazonas State, were used for the manufacture of laboratory particleboards at two density levels of 0.600 and and 0.800 g / cm3, at 8% formaldehyde urea resin content, 7% ammonium sulphate solution content as the catalyst at 30% of concentration, 12% mat moisture content, and at two pressing time periods of 7 and 20 minutes. Physical and mechanical properties of the particleboards were evaluated according to the specifications established by DIN Standards and COVENIN Norm 847.91. The physical properties were the absorption and thickness swelling at 2 and 24 hours by water immersion test, the mechanical properties were determined by static bending test (MOR) and by the tension perpendicular to the board surface tests (IB). The physical properties of water absorption at 2 and 24 hours of immersion for boards of density 0,600 g / cm3 do not comply with the requirements demanded by the DIN Nor and COVENIN Norm 847.91. The water absorption at 24 hours of immersion for boards of density 0.600 g / cm3 do not comply with the value maxim of 25% demanden by the Norms, the boards of density 0.800 g / cm3 at 24 hours of inmersion meet the requeriment demanded by the Norms. The thickness swelling at 2 hours of immersion for boards of density 0.600 g / cm3 and 0.800 g / cm3 do noy comply with the requeriment demanded by the norms. The thickness swelling at 24 hours for boards with density of 0,600 g/cm3 and 0,800 g/cm3 meet the requeriments demanded by the DIN Norm and COVENIN Norm 847.91. The obtained values of the mechanical properties of static bending and tension perpendicular to the board surface a density of 0.600 g / cm3 and 0.800 g / cm3, meet the requirements demand by the DIN Norm and COVENIN Norm 847.91 results of the physical and mechanical properties for the treated CCA particleboards with a density of 0,600 g/cm3, at the three concentration levels of the CCA solution of 0.5, 1.0 and 1.5% respectively, do not comply with the requeriment demanded by the DIN Norm and COVENIN Norm 847.91. On the other hand, the results for the treated CCA particleboards with a density of 0.800 g/cm3, at the three concentration levels of the CCA solution of 0.5, 1.0 and 1.5% respectively meet the requeriments demanded by the DIN Norm and COVENIN Norm 847.91. |
Colación | 47-74 |
Periodicidad | Semestral |
Página Web | http://www.saber.ula.ve/forestalatinoamericana/ |
País | Venezuela |
Institución | Universidad de Los Andes |
Sección | Revista Forestal Latinoamericana: Artículos |